Richards Thermocouple Cat17 Brn

Angle Assemblies - Metal Tubes and Elbow -Types E, J, K & N

Easy to Order - 1 - State quantity 2 - Specify the part number

Example: The part number 8K6-1012XH-12-18-SH signifies an gauge, Type K, angle Assembly , 12” long hot leg made from 1/2” NPT Extra Heavy #10 alloy tube (32% Nickel-21% Chromium), 18” long cold leg made from a steel balance pipe, and a Standard Head. Other combinations of thermocouples and tubes can be specified depending on your application. ! Note: If you would like to order a Type E, J, or N assembly, just substitute the “ K ” with an E, J, or N in the part numbers listed on this page.

(ours or competitive) 3 - Specify the hot ( H ) and cold leg ( C ) lengths. Multiples of 6” (152.4 mm) starting at 12” are stocked 4 - Add letters for mounting attachments 5 - For Double Element Assembly add a “ D ” to the part number. 8K6D-601-12-18-SH

Typical

Protection

Wire

Pipe

Outside Diameter

Application

Tube

Gauge

Size

Type K

Inches

mm

601 Maximum service temperature 2300°F (1260°C) in oxidizing atmospheres. good resistance to sulfidizing atmospheres. 446SS Maximum service temperature 2100°F (1150°C) in oxidizing atmospheres. Excellent resistance to sulfidizing atmospheres , corrosion, scaling, and abrasion.

#6 Seamless Nickel Alloy (601) Nickel 60.5%, Chromium 23% Iron 14%, Aluminum 1.4% Copper .5%, Manganese .5% Silicon .2%, Carbon .05% #7 Seamless Stainless Steel (446) Chromium 23-27% Manganese 1.5% Silicon 1%, Nitrogen .25% Carbon .20%, Sulphur .030% Phosphorous .040% Iron (Balance) #8 Seamless Stainless Steel (304) Chromium 19% Nickel 10%, Manganese 2% Silicon 1%, Carbon .08% Phosphorous .045%

8K6-601-H-C-SH 8K6-634-H-C-SH 8K6-634SP-H-C-SH 8K6-622-H-C-SH 11K6-638-H-C-SH 8K6-701-H-C-SH 8K6-734XH-H-C-SH 8K6-734SP-H-C-SH 8K6-722-H-C-SH 14K6-712SP-H-C-SH 11K6-738-H-C-SH 14K6-738-H-C-SH 8K6-834-H-C-SH 8K6-834XH-H-C-SH 8K6-834SP-H-C-SH 8K6-812XH-H-C-SH 11K6-838-H-C-SH 14K6-838-H-C-SH 11K6-814-H-C-SH 14K6-814-H-C-SH 14K6-818-H-C-SH 8K6-901-H-C-SH 8K6-934-H-C-SH 8K6-934XH-H-C-SH 8K6-934SP-H-C-SH 8K6-922-H-C-SH 8K6-912XH-H-C-SH 11K6-938-H-C-SH 14K6-938-H-C-SH 11K6-914-H-C-SH 14K6-914-H-C-SH 14K6-918-H-C-SH

8 8 8 8 11

1” Std 3/4” Std 3/4” NPT 1/2” Std 3/8” Std 1” Std 3/4” XH 3/4” NPT 1/2” Std 1/2” NPT 3/8” Std 3/8” Std 3/4” Std 3/4” XH 3/4” NPT 1/2” XH 3/8” Std 3/8” Std 1/4” Std 1/4” Std 1/8” Std 1” Std 3/4” Std 3/4” XH 3/4” NPT 1/2” Std 1/2” XH 3/8” Std 3/8” Std 1/4” Std 1/4” Std 1/8” Std

1.32 1.05 1.25

33.4 26.7 31.8 21.3 17.2 33.4 26.7 31.8 21.3 25.4 13.7 17.2 26.7 26.7 31.8 21.2 17.2 17.2 13.7 13.7 10.3 33.4 26.7 26.7 31.8 21.3 21.3 17.2 17.2 13.7 13.7 10.3

.84 .68

8 8 8 8

1.32 1.05 1.25 .84 1.00

14 11 14

.54 .68

8 8 8 8

1.05 1.05 1.25

304SS Maximum service temperature 1600°F (871°C) in oxidizing atmospheres.

.84 .68 .68 .54 .54 .41

11 14 11 14 14

Sulphur .030% Iron (Balance)

8 8 8 8 8 8

1.32 1.05 1.05 1.25

#9 Seamless Nickel Alloy (600) Nickel 76% Chromium 15.5% Iron 8% Manganese .5%

600 Maximum service temperature 2100°F (1150°C) in oxidizing atmospheres. Avoid sulfidizing atmospheres.

.84 .84 .68 .68 .54 .54 .41

11 14 11 14 14

Silicon .2%, Copper .2% Carbon .08%

800 Maximum service temperature 2100°F (1150°C) in oxidizing or reducing atmospheres. Good resistance to sulfidizing atmospheres.

#10 Seamless Nickel Alloy (800) Nickel 35%, Chromium 23% Iron 39.5%, Manganese 1.5%

8K6-1001-H-C-SH 8K6-1034-H-C-SH 8K6-1012XH-H-C-SH

8 8 8

1” Std 3/4” Std 1/2” XH

1.32 1.05 .84

33.4 26.7 21.3

Silicon 1%, Copper .75% Aluminum & Titanium .6% Carbon .1%

Cold leg of thermocouple = C Hot Leg of Thermocouple = H

Page 62