Metal Tubes - Nominal Pipe Thread (NPT)

Richards metal thermocouple protection tubes are manufactured using our special processes to maximize the tube service life. This is evident by our uniquely shaped, heavy mass tips which have been proven in the field for years. Prior to shipment, each tube goes through our Hydro-Pneumatic testing to check for porosity.

Typical

Protection

Pipe

O.D.

I.D.

Lbs/

Kg./

Application

Tube Alloy

Size

Inches mm Inches mm Foot Meter

Type K

214 Maximum service temperature 2200°F (1204°C) in low stress, oxidizing atmospheres. Best used over 1750°F (955°C) and up to 2200°F (1204°C) short

#14 Seamless Nickel Alloy (214) Nickel 75%, Chromium 16% Aluminum 4.5%, Iron 3% Manganese .5%, Silicon 2%, Zirconium 1% Carbon .05%, Yttrium .01%

3/4” Std

1.05

26.7

.82

20.8

1.13

1.68

1434-*

1/2” Std

.84

21.3

.62

15.7

.85

1.27

1422-*

term. Excellent resistance to carburization, Nitriding, and Chlorine attack.

1/4” Std

.54

13.7

.36

9.1

.42

.63

1414-*

316SS Maximum service temperature 1600°F (780°C) in oxidizing atmospheres. Considered better than 304SS on corrosion.

1” Std 3/4” Std 3/4” XH 3/4” NPT 1/2” Std 1/2”XH 3/8” Std 1/4” Std 1/8” Std 1” Std 3/4” Std 1/2” Std 1/4” Std 1/8” Std 1” DXH 1” XH 3/4” XH 1/2” XH 3/8” Std 1/4” Std 1/8” Std

1.32 1.05 1.05 1.25

33.5 26.7 26.7 31.8 21.3 21.3 17.2 13.7 10.4 33.5 26.7 21.3 13.7 10.4 33.5 33.5 26.7 21.3 17.3 13.7 10.4

1.05 .82 .74 .56 .62 .55 .49 .36 .27 1.05 .82 .62 .36 .27

26.7 20.8 18.8 14.2 15.7 14.0 12.4

1.68 1.13 1.47 3.20 .85 1.09

2.50 1.68 2.19 4.76 1.27 1.62

1601-* 1634-*

#16 Seamless Stainless Steel (316) Nickel 10-14%, Chromium 16-18% Molybdenum 2-3%, Manganese 2% Silicon 1%, Phosphorous .045% Carbon .08%, Sulfur .03% #20 Seamless Stainless Steel (310) Chromium 24-26%, Nickel 19-22% Silicon 1.5%, Manganese 2% Carbon .25%, Phosphorous .045% Sulphur .03%, Iron (Balance)

1634XH-* 1634SP-* 1622-* 1612XH

.84 .84 .68 .54 .41

.57 .42 .24

.85 .63 .36

1638-* 1614-* 1618-*

9.1 6.9

310SS Maximum service temperature 2100°F (1150°C) in oxidizing atmospheres. Resists heat scaling Carbon Steel Maximum service temperature 1000°F (540°C) in non-oxidizing applications. Typically used in galvanizing, tin, molten babbit, molten magnesium, petroleum applications and water lines. HR-160 Maximum service temperature 2200°F (1204°C) in oxidizing and reducing atmospheres. Excellent resistance to sulfur, chlorides, and hot corrosion. Typically used in waste incineration. Cast Iron Maximum service temperature 1300°F (700°C) in oxidizing atmospheres. Typically used in molten metal applications Cast Iron, Coated Maximum service temperature 1300°F (700°C) in oxidizing atmospheres. Typically used in molten metal applications

1.32 1.05

26.7 20.8 15.7

1.68 1.13

2.50 1.68 1.27

2001-* 2034-* 2022-* 2014-* 2018-*

.84 .54 .41

.85 .42 .24

9.1 6.9

.63 .36

1.32 1.32 1.05

.60 .96 .74 .55 .49 .36 .27

15.2 24.4 18.8 14.0 12.4

3.1 2.2

4.61 3.27 2.19 1.62

SS01DXH-* SS01XH-* SS34XH-* SS12XH-*

#SS Seamless Carbon Steel Extra Heavy wall ( XH ) Double Extra Heavy wall ( DXH )

1.47 1.09

.84 .68 .54 .41

.57 .42 .24

.85 .63 .36

SS38-* SS14-* SS18-*

9.1 6.9

#160HR Seamless Nickel Alloy Nickel 37%, Cobalt 30%, Chromium 28%, Iron 3.5% Silicon 2.75%, Molybdenum 1% Tungsten 1%, Manganese .5% Titanium .5%, Carbon .05%

3/4” Std 3/4” XH 1/2” Std

1.05 1.05 .84

26.7 26.7 21.3

.82 .74 ..62

20.8 18.8 15.7

1.13 1.47 .85

1.68 2.19 1.27

160HR34-* 160HR34XH-* 160HR22-*

#CI Cast Iron Extra Heavy wall (CIXH) . Cast Iron Protection Tube.

3/4”FNPT 1.63 41.4

.88

22.4

4.8

7.14

CIXH-*

#CIXH-CG Cast Iron Extra Heavy Ceramic Glazed Extra Heavy wall.

3/4”FNPT 1.63 41.4

.88

22.4

4.8

7.14

CIXH-CG-*

Replace the * in the above part numbers with the required length as the suffix. Protection tubes are stocked in multiples of 6 inches starting at 12 inches, although any length can be specified.

Page 92

Phone: 617.527.4385 Fax: 617.964.3746 Email: sales@asrichards.com