Cat16 R2

Angle Assemblies - Metal Tubes - Alloy Bent -Types E, J, K & N - Standard Head (SH)

Easy to Order - 1 - State quantity 2 - Specify the part number

Example: The part number 8K6AB-1012XH-12-18-SH signifies an gauge, Type K, alloy bend angle Assembly , 12” long hot leg made from a bent 1/2” NPT Extra Heavy #10 alloy tube (32% Nickel-21% Chromium), 18” long cold leg made from a steel bal- ance pipe, and a Standard Head ( SH ). Other combinations of thermocouples and tubes can be specified depending on your application. ! Note: If you would like to order a Type E, J, or N assembly, just substitute the “ K ” with an E, J, or N in the part numbers listed on this page.

(ours or competitive) 3 - Specify the hot ( H ) and cold leg ( C ) lengths. Multiples of 6” (152.4 mm) starting at 12” are stocked 4 - Add letters for mounting attachments 5 - For Double Element Assembly add a “ D ” to the part number. 8K6ABD-601-12-18-SH

Typical

Protection

Wire

Pipe

Outside Diameter

Application

Tube

Gauge

Size

Inches

mm

Type K

601 Maximum service temperature 2300°F (1260°C) in oxidizing atmospheres. good resistance to sulfidizing atmospheres. 446SS Maximum service temperature 2100°F (1150°C) in oxidizing atmospheres. Excellent resistance to sulfidizing atmospheres , corrosion, scaling, and abrasion.

#6 Seamless Nickel Alloy (601) Nickel 60.5%, Chromium 23% Iron 14%, Aluminum 1.4% Copper .5%, Manganese .5% Silicon .2%, Carbon .05% #7 Seamless Stainless Steel (446) Chromium 23-27% Manganese 1.5% Silicon 1%, Nitrogen .25% Carbon .20%, Sulphur .030% Phosphorous .040% Iron (Balance) #8 Seamless Stainless Steel (304) Chromium 19%, Nickel 10%, Manganese 2% Silicon 1%, Carbon .08% Phosphorous .045%

8 8 8

1” Std 3/4” Std 1/2” Std 3/8” Std 3/8” Std

1.32 1.05

33.4 26.7 21.3 17.2 17.2

8K6AB-601-H-C-SH 8K6AB-634-H-C-SH 8K6AB-622-H-C-SH 11K6AB-638-H-C-SH 14K6AB-638-H-C-SH

.84 .68 .68

11 14

8 8 8

1” Std 3/4” XH 1/2” Std 3/8” Std 3/8” Std 1/4” Std 3/4” Std 3/4” XH 1/2” XH 3/8” Std 3/8” Std 1/4” Std 1/4” Std 1/8” Std 1” Std 3/4” Std 3/4” XH 1/2” Std 1/2” XH 3/8” Std 3/8” Std 1/4” Std 1/4” Std 1/8” Std

1.32 1.05

33.4 26.7 21.3 13.7 17.2 13.7 26.7 26.7 21.2 17.2 17.2 13.7 13.7 10.3 33.4 26.7 26.7 21.3 21.3 17.2 17.2 13.7 13.7 10.3

8K6AB-701-H-C-SH 8K6AB-734XH-H-C-SH 8K6AB-722-H-C-SH 11K6AB-738-H-C-SH 14K6AB-738-H-C-SH 14K6AB-714XH-H-C-SH 8K6AB-834-H-C-SH 8K6AB-834XH-H-C-SH 8K6AB-812XH-H-C-SH 11K6AB-838-H-C-SH 14K6AB-838-H-C-SH 11K6AB-814-H-C-SH 14K6AB-814-H-C-SH 14K6AB-818-H-C-SH 8K6AB-901-H-C-SH 8K6AB-934-H-C-SH 8K6AB-934XH-H-C-SH 8K6AB-922-H-C-SH 8K6AB-912XH-H-C-SH 11K6AB-938-H-C-SH 14K6AB-938-H-C-SH 11K6AB-914-H-C-SH 14K6AB-914-H-C-SH 14K6AB-918-H-C-SH

.84 .54 .68 .54

11 14 14

8 8 8

1.05 1.05

304SS Maximum service temperature 1600°F (871°C) in oxidizing atmospheres.

.84 .68 .68 .54 .54 .41

11 14 11 14 14

Sulphur .030% Iron (Balance)

8 8 8 8 8

1.32 1.05 1.05

#9 Seamless Nickel Alloy (600) Nickel 76% Chromium 15.5% Iron 8% Manganese .5%

600 Maximum service temperature 2100°F (1150°C) in oxidizing atmospheres. Avoid sulfidizing atmospheres.

.84 .84 .68 .68 .54 .54 .41

11 14 11 14 14

Silicon .2%, Copper .2% Carbon .08%

800 Maximum service temperature 2100°F (1150°C) in oxidizing or reducing atmospheres. Good resistance to sulfidizing atmospheres.

#10 Seamless Nickel Alloy (800) Nickel 35%, Chromium 23% Iron 39.5%, Manganese 1.5%

8 8 8

1” Std 3/4” Std 1/2” XH

1.32 1.05 .84

33.4 26.7 21.3

8K6AB-1001-H-C-SH 8K6AB-1034-H-C-SH 8K6AB-1012XH-H-C-SH

Silicon 1%, Copper .75% Aluminum & Titanium .6% Carbon .1%

Cold leg of thermocouple = C Hot Leg of Thermocouple = H

Page 66